316 / 316L Stainless Ornamental Tubing

Part of the austenitic family of stainless steel, both 316 and 316L stainless ornamental tubing contain slightly more nickel than T304/304L, as well as 2-3% molybdenum. This allows for better corrosion resistance than T304, especially in environments that tend to cause pitting. It is widely used in the chemical processing industries.

Don’t see what you need? Request a Quote

SKU	Description	DFARS	Manufacture Method	OD	Wall	Specification
Sku: 38989	Description: W316L ORN 1 SQ X .120	DFARS: Yes	Manufacture Method: WELDED & DRAWN	OD: 1.0000	Wall: 0.1200	Specification: ASTM A554
Sku: 38995	Description: W316L ORN 1-1/4 SQ X.145	DFARS: No	Manufacture Method: WELDED & DRAWN	OD: 1.2500	Wall: 0.1450	Specification: ASTM A554
Sku: 03103	Description: W 316/L ORN 1-1/2 SQ X .120 WA	DFARS: Yes	Manufacture Method: WELDED & DRAWN	OD: 1.5000	Wall: 0.1200	Specification: ASTM A554
Sku: 47031	Description: W316/L ORN 2 SQ X .120 WA	DFARS: No	Manufacture Method: WELDED & DRAWN	OD: 2.0000	Wall: 0.1200	Specification: ASTM A554
Sku: 39029	Description: W 316L ORN 2 SQ X .250 WA	DFARS: Yes	Manufacture Method: WELDED & DRAWN	OD: 2.0000	Wall: 0.2500	Specification: ASTM A554
Sku: 39027	Description: W 316L ORN 2 SQ X .180	DFARS: Yes	Manufacture Method: WELDED & DRAWN	OD: 2.0000	Wall: 0.1800	Specification: ASTM A554
Sku: 39043	Description: W 316L ORN 3 SQ X .250 WA	DFARS: Yes	Manufacture Method: WELDED & DRAWN	OD: 3.0000	Wall: 0.2500	Specification: ASTM A554
Sku: 25448	Description: W 316L ORN 2-1/2 SQ X .180 WA	DFARS: Yes	Manufacture Method: WELDED & DRAWN	OD: 2.5000	Wall: 0.1800	Specification: ASTM A554
Sku: 22680	Description: W316/316L ORN 5 SQ X .250 WA	DFARS: No	Manufacture Method: WELDED & DRAWN	OD: 5.0000	Wall: 0.2500	Specification: ASTM A554

Stock Size Range:

Squares - 1/2" OD - 6" OD Wall Thickness - .065 - .180
Rectangles - 1/2" x 1" to 6" Wall Thickness - .065 - .250

Typical Chemical Composition % (Max Values, Unless Noted)
Weight %	C	Mn	P	S	Si	Cr	Ni	Moly
316	0.08	2.00	.045	.030	1.00	16.0-18.0	10.0-14.0	2.0-3.0
316L	.035	2.00	.045	.030	1.00	16.0-18.0	10.0-15.0	2.0-3.0

Typical Mechanical Properties
Grade	Tensile
	Ultimate/Min		Yield/Min		Elongation/Min
	KSI	MPA	KSI	MPA	%
316	75	517	30	207	35
316L	70	483	25	172	35